PRACA ORYGINALNA
Obróbka stopów wykorzystywanych do wykonywania protez szkieletowych. Polerowanie elektrochemiczne w wybranych elektrolitach
1
Medical University of Warsaw
Prosthodontics 2014;64(5):354-360
SŁOWA KLUCZOWE
REFERENCJE (22)
1.
Bezzon O.L., Pedrazzi H., Zaniquelli O., da Silva T.B.: Effect of casting technique on surface roughness and consequent mass loss after polishing of NiCr and CoCr base metal alloys: a comparative study with titanium. J. Prosthet. Dent., 2004, 92, 274-277.
2.
Bollen C.M., Papaioanno W, Van Eldere J, Schepers E, Quirynen M, van Steenberghe D.: The influence of abutment surface roughness on plaque accumulation and peri – implant mucositis. Clin. Oral Implants Res., 1996, 7, 201-211.
3.
Bridgeport D.A, Brantley W.A, Herman P.F.: Cobalt-chromium and nickel-chromium alloys for removable prosthodontics, part 1: mechanical properties. J. Prosthodont., 1993, 2, 144-150.
4.
de Melo J.F, Gjerdet N. R, Erichsen E.S.: Metal release from cobalt – chromium partial dentures in the mouth. Acta Odontol. Scand., 1983, 41, 71-74.
5.
Grossner-Schreiber B., Griepentrog M., Haustein I., Müller W.D., Lange K.P., Briedigkeit H., Göbel U.B.: Plaque formation on surface modified dental implants. Clin. Oral Implants Res., 2001, 12, 543-551.
6.
Guilherme A.S., Henriques G.E., Zavanelli R.A., Mesquita M.F.: Surface roughness and fatigue performance of commercially pure titanium and Ti-6Al-4V alloy after different polishing protocols. J. Prosthet. Dent., 2005, 93, 378-385.
7.
Hassan L, Juszczyk A.S, Clark R.K.F.: Immediate replacement removable partial dentures with cobalt – chromium frameworks: rationale, technology and a case report. J. Oral Rehabil., 2005, 32, 772-775.
8.
Hirata T., Nakamura T., Takashima F., Maruyama T., Taira M., Takahashi J.: Studies on polishing of Ti and Ag-Pd-Cu-Au alloy with five dental abrasives. J. Oral Rehabil., 2001, 28, 773-777.
9.
Jang K.S, Youn S.J, Kim Y.S.: Comparison of castability and surface roughness of commercially pure titanium and cobalt – chromium denture frameworks. J. Prosthet. Dent., 2001, 86, 93-98.
10.
Janukiewicz T.: Elektrolityczne polerowanie protez szkieletowych ze stopów chromo-kobaltowych. Protet. Stomatol., 1975, 1, 53-60.
11.
Jumer J.F.: Surface TreatmentsElectropolishing. Metal Finishing Guidebook Directory Jan., 1988.
12.
Kohal R.J., Bächle M., Emmerich D., Beschnidt S.M., Strub J.R.: Hard tissue reaction to dual acid – etched titanium implants: influence of plaque accumulation. A histological study in humans. Clin. Oral Implants Res., 2003, 14, 381-390.
13.
Kuhar M., Funduk N.: Effects of polishing techniques on the surface roughness of acrylic denture base resins. J. Prosthet. Dent., 2005, 93, 76-85.
14.
Quirynen M, Bollen C.M.: The influence of surface roughness and surface-free energy on supra- and subgingival plaque formation in man. J. Clin. Periodontol., 1995, 22, 1-14.
15.
Radford D.R., Sweet S.P., Challacombe S.J., Walter J.D.: Adherence of candida albicans to denture – base materials with different surface finishes. J. Dent., 1998, 26, 577-583.
16.
Sen D., Goller G., Issever H.: The effect of two polishing pastes on the surface roughness of bis – acryl composite and methacrylate – based resins. J. Prosthet. Dent., 2002, 88, 527- 532.
17.
Sinclair G.F., Radford D.R., Sherriff M., Walter J.D.: Effects of electrobrightening on the fit surface of cobalt – chromium RPD frameworks. Int. J. Prosthodont., 2000, 13, 232-237.
18.
Spiechowicz E.: Protetyka stomatologiczna. Wydawnictwo Lekarskie PZWL, Warszawa 2004.
19.
Taga Y., Kawai K., Nokubi T.: New method for divesting cobalt – chromium alloy castings: sandblasting with a mixed abrasive powder. J. Prosthet. Dent., 2001, 85, 357-362.
20.
Taylor R., Maryan C., Verran J.: Retention of oral microorganisms on cobalt – chromium alloy and dental acrylic resin with different surface finishes. J. Prosthet. Dent., 1998, 80, 592-597.
21.
Wataha J.C., Lockwood P.E., Khajotia S.S., Turner R.: Effect of pH on element release from dental casting alloys. J. Prosthet. Dent., 1998, 80, 691-698.
22.
Gupta K.P.: The Co-Cr-Mo (CobaltChromium-Molybdenum) system. J. Phase Equilibria and Diffusion, 2005, 26, 87-92.
| eISSN: | 2391-601X |
| ISSN: | 0033-1783 |
Przetwarzamy dane osobowe zbierane podczas odwiedzania serwisu. Realizacja funkcji pozyskiwania informacji o użytkownikach i ich zachowaniu odbywa się poprzez dobrowolnie wprowadzone w formularzach informacje oraz zapisywanie w urządzeniach końcowych plików cookies (tzw. ciasteczka). Dane, w tym pliki cookies, wykorzystywane są w celu realizacji usług, zapewnienia wygodnego korzystania ze strony oraz w celu monitorowania ruchu zgodnie z Polityką prywatności. Dane są także zbierane i przetwarzane przez narzędzie Google Analytics (więcej).
Możesz zmienić ustawienia cookies w swojej przeglądarce. Ograniczenie stosowania plików cookies w konfiguracji przeglądarki może wpłynąć na niektóre funkcjonalności dostępne na stronie.
Możesz zmienić ustawienia cookies w swojej przeglądarce. Ograniczenie stosowania plików cookies w konfiguracji przeglądarki może wpłynąć na niektóre funkcjonalności dostępne na stronie.